Descriptif neutre pour cahier des charges. |
|
|
|
|
|
|
|
Propriétés physiques |
|
|
|
|
|
|
|
| . |
. |
Simple vitrage
SGG PRIVA-LITE®
Composition standart (12mm)
|
|
Double vitrage SGG PRIVA-LITE®
Composition standart (12mm)
12 mm air /
6 mm SKN 172
|
|
Double vitrage SGG PRIVA-LITE®
Composition standart (12mm)
15 mm argon /
6 mm PLT FUTUR N
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ON |
|
OFF |
|
ON |
|
OFF |
|
ON |
|
OFF |
|
|
|
|
|
|
|
|
|
|
|
|
|
TL*
|
77%
|
|
76%
|
|
53% |
|
54% |
|
62% |
|
63% |
| . |
. |
|
. |
|
|
|
|
|
|
|
|
|
RL*
|
19%
|
|
18%
|
|
20%
|
|
20%
|
|
21% |
|
21% |
| . |
. |
|
. |
|
|
|
|
|
|
|
|
|
FS*
|
63%
|
|
64%
|
|
41%
|
|
41%
|
|
46% |
|
46% |
|
|
|
|
|
|
|
|
|
|
|
|
|
| U* |
|
5,6 to 5,8
W/m2k |
|
5,6 to 5,8
W/m2k |
|
1,6
W/m2k |
|
1,6
W/m2k |
|
1,1
W/m2k |
|
1,1
W/m2k |
|
|
|
|
|
|
|
|
|
|
|
|
|
| flou* |
|
<7,5% |
|
>90% |
|
<8,5% |
|
>90% |
|
<8,4% |
|
>90% |
|
|
*les valeurs spectrophotométriques sont données dans une plage de +/- 2%
|
|
|
|
|
|
|
Produit verrier à opacification commandée, du type SGG PRIVA-LITE® de Saint-Gobain Glass, non transparent à la vision, pouvant être rendu transparent par l’application d’un champ électrique d’approximativement 100 V AC.
Il s'agit d’un verre feuilleté composé d’au moins deux feuilles de verre extra claire, et d’au moins deux films intercalaires entre lesquels est placé un film à cristaux liquides (LC). Ces composants sont assemblés pour former un ensemble compact.
Au repos, les cristaux liquides, en position désordonnée, donnent au vitrage un aspect translucide qui empêche la vision. Sous l’influence d’un champ électrique, ces cristaux liquides s'alignent, le vitrage devient alors transparent et permet la vision. Le passage entre l’état translucide et l’état transparent est presque immédiat.
|
|
| TL |
=
|
Transmission lumineuse |
|
|
|
| RL |
=
|
Réflexion lumineuse |
|
|
|
| FS |
=
|
Facteur solaire |
|
|
|
| U |
=
|
valeur U |
|
|